PolyMide™ PA6-CF Carbon Fiber Reinforced Nylon - 1.75mm | Polymaker

Polymaker PolyMide™ PA6-CF (carbon fiber reinforced nylon)

PolyMide™ PA6-CF is a 20% carbon fiber reinforced Nylon 6 filament. The carbon fiber reinforcement provides significantly improved stiffness, strength and heat resistance with outstanding layer adhesion thanks to Fiber Adhesion™ Technology. PolyMide™ PA6-CF offers durability and functionality while featuring a heat deflection temperature of 215°C.

Color: Black
Diameter: 1.75mm
Weight: 500g

Note: Use of a wear resistant nozzle is recommended

Print Settings:
Nozzle: 280˚C – 300˚C
Bed: 25˚C – 50˚C
Fan Speed: Off
Print Speed: 30mm/s – 60mm/s
Print Surface: Glass, PEI, BuildTak with a coat of Magigoo Pro PA 
Direct Drive: Retraction Distance: 3mm
Indirect Drive: Retraction Distance: 6mm

Annealing settings: 80˚C for 6h

Drying settings: 100˚C for 8 hours (only if the material has absorbed moisture)

Mechanical Properties
Young’s Modulus: 7453 ± 656 (MPa)
Tensile Strength: 105.0 ± 5.0 (MPa)
Bending Strength: 169.0 ± 4.7 (MPa)
Charpy Impact Strength: 13.34 ± 0.52 (kJ/m2)

Thermal Properties
Heat Deflection Temperature (ISO 75 1.8 MPa): 196 ˚C
Heat Deflection Temperature (ISO 75 0.45 MPa): 215 ˚C
Melting Temperature: 220 (°C)

PolyMide™ PA6-CF Technical Data Sheet